FePt films were prepared on (100) oriented single crystal MgO substrates at high temperature ranging from 620 until 800 °C and in-situ annealed for different times ranging from 0 to 60 min to obtain ordered FePt films. The structural analysis indicates that FePt films grow epitaxially on MgO (100) substrates. Both increasing deposition temperature and in-situ annealing time enhance the (001) texture and ordering of FePt films. The magnetic analysis shows that these L10 FePt films have perpendicular anisotropy and the easy magnetization c-axis is perpendicular to the film plane. Magnetization reversal is controlled by a rotational mechanism. The hard magnetic properties of the films are improved with increasing deposition temperature or in-situ annealing time.