Magnetic and structural properties of CoCrTa films and multilayers with Cr

D. J. Sellmyer, D. Wang, J. A. Christner

Research output: Contribution to journalArticle

10 Scopus citations

Abstract

We report our studies of epitaxial growth of CoCrTa films on Cr underlayers and the properties of CoCrTa/Cr multilayers. The coercivity, Hc, strongly depends on Ta composition, sputtering conditions, and the thicknesses of the magnetic layer and Cr underlayer. An Hc value of 1300 Oe was obtained for a Ta composition of 2 at. %, a Cr underlayer thickness of 4000 Å, and a magnetic layer thickness of 400 Å. The x-ray data show that the high Hc occurs when crystallites of the Cr underlayer and CoCrTa layer are aligned with the Cr (200) and CoCrTa (110) planes in the film plane. Thus, the c axis of the CoCrTa lies essentially in the plane of the film. When the thickness of the magnetic layer increases above 1000 Å the c axis begins to tip out of the film plane. The basal plane lattice parameter varies roughly linearly with Ta content up to 13 at. %. For the CoCrTa/Cr multilayered films, Hc values up to 1200 Oe were obtained although the c-axis orientation of the magnetic layer becomes somewhat dispersed. Models for the dependence of magnetization reversal on microstructure are discussed.

Original languageEnglish (US)
Pages (from-to)4710-4712
Number of pages3
JournalJournal of Applied Physics
Volume67
Issue number9
DOIs
StatePublished - 1990

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Magnetic and structural properties of CoCrTa films and multilayers with Cr'. Together they form a unique fingerprint.

  • Cite this