Magnetic properties of Nd(Fe,Ti)12 and Nd(Fe,Ti) 12Nx films of perpendicular texture

D. Wang, D. J. Sellmyer, I. Panagiotopoulos, D. Niarchos

Research output: Contribution to journalArticlepeer-review

3 Scopus citations


Nd(Fe,Ti)12 and Nd(Fe,Ti)12Nx films textured with c axis perpendicular to the film plane were synthesized by sputtering. For the Nd(Fe,Ti)12 films a spin reorientation took place at about 170 K. For the Nd(Fe,Ti)12Nx films, the anisotropy field is about 85 kOe at room temperature and 130 kOe at 5 K, corresponding to a coercivity of 2.7 and 12 kOe, respectively. Initial magnetization curves show a behavior characteristic of nucleation type of magnetization reversal mechanism. Attempts were made to fit the experimental data with Kronmüller's magnetization reversal model. The results suggest that nucleation with extended sites is responsible for the reversal.

Original languageEnglish (US)
Pages (from-to)6232-6234
Number of pages3
JournalJournal of Applied Physics
Issue number10
StatePublished - 1994

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Magnetic properties of Nd(Fe,Ti)<sub>12</sub> and Nd(Fe,Ti) <sub>12</sub>N<sub>x</sub> films of perpendicular texture'. Together they form a unique fingerprint.

Cite this